Density 密度 [g/cm3] |
Young's Modulus ヤング率 [GPa] |
Tensile Strength (Yield) 降伏強さ [MPa] |
Tensile Strength (Ultimate) 引張強さ [MPa] |
Shear Modulus ずれ弾性率 [GPa] |
Elongation at Break 伸び [%] |
Q Factor Q値 |
文献 |
Maraging Steel Fe-17.5, Ni-12.5, Co-3.75, Mo-1.8, Ti-0.15, Al |
8.0 |
186 @300K |
2379 @300K |
2689 @300K |
|
5-10 @300K |
|
MAD |
2800 Maraging Steel Fe-17.9, Ni-14.8, Co-6.69, Mo-1.1, Ti |
8.0 |
|
2693 |
2617 |
|
6.0 |
|
Matweb |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|